Glass ionomer cements (GICs) are products of the acid-base setting reaction between an finely fluoro-alumino silicate glass powder and poly(acrylic acid) in aqueous solution. The sol gel method is an adequate route of preparation of the glasses used to obtain the GICs. The objective of this paper was to compare two powders: a commercial and an experimental and to investigate the structural changes during hardening of the cements by FTIR and Al MAS NMR. These analyses showed that the experimental glass powder reacted with organic acid to form the GICs and it is a promising material to manufacture dental cements.

Glass ionomer cements are glass and polymer composite materials. These materials currently find use in dentistry. The purpose of this work is to obtain glass powders based on the composition 4.5SiO2 - 3Al2O3 - 2CaO to be used in dentistry. The powders were prepared by a chemical route at 700 0C. The properties of glass ionomer cements obtained from powders prepared at 700 ºC were studied. Diametral tensile strength and microhardness were evaluated for the experimental glass ionomer cements and a commercial material. It was concluded that the properties of experimental cements were similar to those of the commercial ones.